Home »About us »Material Selection
| Trademark | Material Code | The main purpose |
| F30%CrMo | Cr30 | Amounted to 35% solids is corrosive media ideal timber, such as phosphoric acid extraction and other similar corrosive slurry abrasive media, the current Bureau of the leading domestic level. |
| 1Cr18Ni9Ti | 18-8 | Lye, acetic acid, dilute nitric acid |
| 00Cr14Ni14Si4 | C4 | Full concentration of nitric acid, especially for concentrated nitric acid, nitric acid is concentrated integrated steel casting material best. |
| 00Cr20Ni25Mo4 | UB6 | With a certain amount of CI-, between F-, SO2 / 4- phosphoric acid, sulfuric acid and high temperature, resistance to pitting and intergranular corrosion. |
| 0Cr12Ni25Mo3Cu3Si2Nb | 941 | Full concentration of sulfuric acid at room temperature, especially for the 100 ° C or less moderate concentration (about 50%) sulfuric acid. |
| 00Cr10Ni20Mo1.5Si6Cu | SS920 | Hot concentrated sulfuric acid, t≤130 ° C, the concentration of 93-98%. |
| 00Cr21Ni32Mo2Cu3 | 20#Alloy | Hot concentrated sulfuric acid, t≤130 ° C, the concentration of about 40%. |
| Z180C13 | DF2 | Amounted to 70% solids abrasive media |
| 0Cr26Ni5Mo2Cu3 | CD-4MCu | Solid sulfuric acid, phosphoric acid, wear and corrosion. |
| 0Cr24Ni20Mo2Cu3 | K Alloy | ≤60°C Various concentrations of sulfuric acid. |
| 00Cr25Ni6Mo2 | MM-4 | Nitrate fertilizer special steel |
| 0Cr18Ni9 | 304 | Dilute nitric acid, an organic acid. |
| 00Cr18Ni9 | 304L | Dilute nitric acid, organic acids, resistance to intergranular corrosion. |
| 0Cr18Ni12Mo2Ti | Mo2Ti | Dilute nitric acid, phosphoric acid, an organic acid. |
| 0Cr18Ni12Mo2 | 316 | Dilute nitric acid, phosphoric acid, an organic acid. |
| 00Cr18Ni12Mo2 | 316L | Dilute nitric acid, phosphoric acid, organic acid, resistance to intergranular corrosion. |
| 0Cr20Ni25Mo5Cu2 | 904 | 70 ° C under a variety of concentrated sulfuric acid, resistance to intergranular corrosion. |
|
0Cr30Ni42Mo3Cu2 |
804 | 904 still resists caustic soda evaporation and so on. |
| 0Cr20Ni42Mo3Cu32 | 824 | 904 still resists media. |
| 0Cr18Ni5Mo5 | NH55 | Seawater. |
| 0Cr20Ni33Mo3Cu3Nb | 20Cb3 | Various concentrations of sulfuric acid corrosion. |
| 0Cr24Ni33Mo2.5Cu3Ti | 3#4# | Containing various concentrations of sulfuric acid. |
| 0Cr16Ni4Cu3Nb | CB-7Cu | Mortar abrasion, potash production during grinding, corrosion. |
| 00Cr30Ni40Mo4Cu3 | Lewmet55 | 125 ° C temperature fuming sulfuric acid corrosion. |
| 00Ni65Cu28 | Monel | Hydrofluoric acid, hydrofluoric acid silicon, high temperature caustic soda. |
| 00Ni65Mo28 | Hastelloy B | Full concentration of hydrochloric acid |
| Plastic FEP | F46 | Various acids, alkalis, salts, oxidants and other media. |
| UHMWPE | Below 80 ° C containing suspended solids of acid, alkali, salt, medium. |